Color Stability, Surface Roughness and Flexural Strength of an Acrylic Resin Submitted to Simulated Overnight Immersion in Denture Cleansers

This study evaluated color stability, surface roughness and flexural strength of acrylic resin specimens after immersion in alkaline peroxide and alkaline hypochlorite, simulating a period of one and a half year of use of overnight immersion. Sixty disc-shaped (16X4 mm) and 80 rectangular specimens (65X10X3.3 mm) were prepared from heat-polymerized acrylic resin (Lucitone 550) and distributed into 4 groups (n=20): C1: without immersion, C2: 8 h immersion in distilled water; AP: 8 h immersion in alkaline peroxide effervescent tablet; SH: 8 h immersion in 0.5% NaOCl solution. Properties were evaluated at baseline and after the immersion. Color data were also calculated according the National Bureau of Standards (NBS). Results were analyzed statistically by ANOVA and Tukey's HSD test (α=0.05). AP (2.34 ± 0.41) caused color alteration significantly higher than C2 (0.39 ± 0.30) and SH (1.73 ± 0.52). The mean ΔE values were classified as indicial for C2 (0.36 ± 0.29) and noticeable for AP (2.12 ± 0.39) and SH (1.59 ± 0.48). SH (0.0195 ± 0.0150) caused significantly higher ΔRa (p=0.000) than the C2 (0.0005 ± 0.0115) and PA (0.0005 ± 0.0157) groups. There was no statistically significant difference (p=0.063) among the solutions for flexural strength (C1: 105.43 ± 14.93, C2: 100.30 ± 12.43, PA: 97.61 ± 11.09, SH: 95.23 ± 10.18). In conclusion, overnight immersion in denture cleansing solutions simulating a year and a half of use did not alter the flexural strength of acrylic resin but caused noticeable color alterations, higher for alkaline peroxide. The 0.5% NaOCl solution caused increase in surface roughness.

Resumo O estudo avaliou a alteração de cor, rugosidade de superfície e força de flexão de espécimes de resina acrílica após imersão em peróxido alcalino e hipoclorito alcalino, simulando um ano e meio de uso seguindo a imersão noturna. Sessenta espécimes circulares (16 X 4 mm) e oitenta retangulares (65 X 10 X 3,3 mm) de resina acrílica termopolimerizável (Lucitone 550) foram distribuídos em 4 grupos (n=20): C1: sem imersão, C2: 8 h de imersão em água destilada; PA: 8 h de imersão em pastilhas efervescentes de peróxido alcalino; HS: 8 h de imersão em hipoclorito de sódio a 0,5%. As propriedades foram avaliadas antes e após as imersões. Os dados de alteração de cor também foram calculados de acordo com o National Bureau of Standards (NBS). Os dados foram analisados estatisticamente pelo teste ANOVA e Tukey HSD (α=0,05). O PA (2,34 ± 0,41) causou alteração de cor significativamente maior que C2 (0,39 ± 0,30) e SH (1,73 ± 0,2). A média ΔE foi classificada como indicial para C2 (0,36 ± 0,29) e perceptível para PA (2,12 ± 0,39) e HS (1,59 ± 0,48). HS (0,0195 ± 0,0150) causou significantemente maior ΔRa (p=0) do que os demais (C2: 0,0005 ± 0,0115 e PA: 0,0005 ± 0,0157). Não houve diferença estatisticamente significante (p=0,063) entre as soluções para a resistência à flexão (C1: 105,43 ± 14,93; C2: 100,30 ± 12,43, PA: 97,61 ± 11,09, HS: 95,23 ± 10,18). A imersão noturna em soluções higienizadores de próteses simulando um ano e meio de uso não alterou a resistência à flexão da resina acrílica, porém causou alterações perceptíveis de cor, sendo maiores com o peróxido alcalino. O hipoclorito de sódio a 0,5% ...

Abrasiveness of conventional and specific denture-cleansing dentifrices

This study analyzed the weight loss and surface roughness caused in Plexiglass specimens by conventional dentifrices (Sorriso, Colgate and Close Up) and specific dentifrices used for cleaning of dentures (Corega and Dentu Creme). Plexiglass specimens were divided into 6 groups (n=6) including: a control (distilled water - DW) and experimental groups. Brushing was performed in a toothbrushing machine with a soft brush and a dentifrice suspension and DW according to different brushing times (50, 100, 200 and 250 min -18,000, 36,000, 72,000 and 90,000 cycles, respectively, calculated to correspond to 1, 2, 4 and 5 years of regular brushing). The results of weight loss and surface roughness were analyzed by ANOVA and Tukey’s test at 5% significance level. In all tested times, the effect of DW was insignificant. Dentifrices differed significantly from DW in the initial period. Corega dentifrice caused greater mass loss in all studied times, followed by Close Up. Dentifrices resulted in a surface roughness similar to the DW at 50 min. In the other times, Sorriso, Colgate and Corega caused more surface roughness than DW. In conclusion, specific dentifrices caused larger mass loss and lower surface roughness as conventional dentifrice.

Este estudo analisou a perda de massa e rugosidade superficial causadas em corpos de prova de Plexiglass por dentifrícios convencionais (Sorriso, Colgate e Close Up) e específicos (Corega e Dentu Creme) para higienização de próteses totais. Os corpos de prova de Plexiglass foram distribuidos em 6 grupos (n=6), sendo um controle (água destilada - AD) e grupos experimentais. A escovação foi realizada em máquina de escovação com escovas macias e suspensões de dentifrícios ou AD, de acordo com os diferentes tempos de escovação (50, 100, 200 e 250 min -18.000, 36.000, 72.000 e 90.000 ciclos, respectivamente, calculados para corresponder a 1, 2, 4 e 5 anos de escovação regular). Os resultados de perda de massa e rugosidade superficial foram analisados por meio de ANOVA e teste de Tukey com 5% de significância. Em todos os tempos analisados, a AD teve efeito insignificante. Os dentifrícios diferiram significativamente da AD no período inicial. O dentifrício Corega causou maior perda de massa em todos os tempos estudados, seguido por Close Up. No tempo de 50 min, todos os dentifrícios causaram rugosidade superficial semelhante à AD. Nos outros tempos, Sorriso, Colgate e Corega causaram maior rugosidade superficial em relação à AD. Conclui-se que os dentifrícios específicos causaram maior perda de massa, porém menor rugosidade superficial que os dentifrícios convencionais.

Effect of denture cleansers on metal ion release and surface roughness of denture base materials

Chemical disinfectants are usually associated with mechanical methods to remove stains and reduce biofilm formation. This study evaluated the effect of disinfectants on release of metal ions and surface roughness of commercially pure titanium, metal alloys, and heat-polymerized acrylic resin, simulating 180 immersion trials. Disk-shaped specimens were fabricated with commercially pure titanium (Tritan), nickel-chromium-molybdenum-titanium (Vi-Star), nickel-chromium (Fit Cast-SB Plus), and nickel-chromium-beryllium (Fit Cast-V) alloys. Each cast disk was invested in the flasks, incorporating the metal disk to the heat-polymerized acrylic resin. The specimens (n=5) were immersed in these solutions: sodium hypochlorite 0.05%, Periogard, Cepacol, Corega Tabs, Medical Interporous, and Polident. Deionized water was used as a control. The quantitative analysis of metal ion release was performed using inductively coupled plasma mass spectrometry (ELAN DRC II). A surface analyzer (Surftest SJ-201P) was used to measure the surface roughness (µm). Data were recorded before and after the immersions and evaluated by two-way ANOVA and Tukey's test (α=0.05). The nickel release proved most significant with the Vi-Star and Fit Cast-V alloys after immersion in Medical Interporous. There was a significant difference in surface roughness of the resin (p=0.011) after immersion. Cepacol caused significantly higher resin roughness. The immersion products had no influence on metal roughness (p=0.388). It could be concluded that the tested alloys can be considered safe for removable denture fabrication, but disinfectant solutions as Cepacol and Medical Interporous tablet for daily denture immersion should be used with caution because it caused greater resin surface roughness and greater ion release, respectively.

Desinfetantes químicos são normalmente associados a métodos mecânicos para remover manchas e reduzir a formação do biofilme. Este estudo avaliou o efeito de desinfetantes na liberação de íons metálicos e na rugosidade superficial do titânio comercialmente puro, ligas metálicas e resina acrílica termopolimerizável, simulando 180 ensaios de imersões. Espécimes em formato de discos foram confeccionados com titânio comercialmente puro (Tritan), liga de níquel-cromo-molibdênio-titânio (Vi-Star), liga de níquel-cromo (Fit Cast-SB Plus) e liga de níquel-cromo-berílio (Fit Cast-V). Os espécimes (n=5) foram imersos nestas soluções: hipoclorito de sódio a 0,05%, Periogard, Cepacol, Corega Tabs, Medical Interporous e Polident. Como controle, foi utilizada a água deionizada. A análise quantitativa de liberação de íons metálicos foi realizada por meio de espectrometria de massa com plasma indutivamente acoplado (ELAN DRC II). O rugosímetro (Surftest SJ-201P) foi utilizado para medir a rugosidade superficial (µm). Os dados foram registrados antes e depois das imersões e avaliados por ANOVA com dois fatores e teste de Tukey (α=0,05). A liberação de níquel provou ser mais expressiva nas ligas Vi-Star e Fit Cast-V após a imersão em Medical Interporous. Houve diferença significante na rugosidade superficial da resina (p=0,011) após a imersão. O Cepacol causou maior rugosidade superficial de forma significativa. Os produtos de imersão não influenciaram nos resultados da rugosidade do metal (p=0,388). Pode-se concluir que as ligas metálicas testadas podem ser consideradas seguras para a fabricação de próteses removíveis, mas as soluções desinfetantes como o Cepacol e a pastilha Medical Interporous para a imersão diária da prótese devem ser utilizados com cautela, pois causaram maior rugosidade superficial da resina e maior liberação de íons, respectivamente.

Effect of different cleansers on the surface of removable partial denture

Removable partial dentures (RPD) demand specific hygienic cleaning and the combination of brushing with immersion in chemical solutions has been the most recommended method for control of biofilm. However, the effect of the cleansers on metallic components has not been widely investigated. This study evaluated the effect of different cleansers on the surface of RPD. Five disc specimens (12 mm x 3 mm metallic disc centered in a 38 x 18 x 4 mm mould filled with resin) were obtained for each experimental situation: 6 solutions [Periogard (PE), Cepacol (CE), Corega Tabs (CT), Medical Interporous (MI), Polident (PO), 0.05 percent sodium hypochlorite (NaOCl), and distilled water (DW) control] and 2 Co-Cr alloys [DeguDent (DD) and VeraPDI (VPDI)] were used for each experimental situation. A 180-day immersion was simulated and the measurements of roughness (Ra, µm) of metal and resin were analyzed using 2-way ANOVA and Tukey’s test. The surface changes and tarnishes were examined with a scanning electronic microscopy (SEM). In addition, energy dispersive x-ray spectrometry (EDS) analysis was carried out at representative areas. Visually, NaOCl and MI specimens presented surface tarnishes. The roughness of materials was not affected by the solutions (p>0.05). SEM images showed that NaOCl and MI provided surface changes. EDS analysis revealed the presence of oxygen for specimens in contact with both MI and NaOCl solutions, which might suggest that the two solutions promoted the oxidation of the surfaces, thus leading to spot corrosion. Within the limitations of this study, it may be concluded that the NaOCl and MI may not be suitable for cleaning of RPD.

As próteses parciais removíveis (PPR) exigem higienização específica e a associação da escovação com imersão em soluções químicas tem sido o método mais recomendado para controle do biofilme. Entretanto, os efeitos destas soluções não são amplamente reportados em componentes metálicos. Este estudo avaliou o efeito de diferentes agentes de higienização na superfície dos componentes de uma PPR. Foram confeccionados 5 espécimes (disco metálico de 12 x 3 mm centralizado em uma tira de resina com 38 x 18 x 4 mm) para cada situação experimental: 6 soluções [Periogard (PE), Cepacol (CE), Corega Tabs (CT), Medical Interporous (MI), Polident (PO), hipoclorito de sódio 0,05 por cento (HS) e água destilada (AD) como controle)] e 2 ligas de cobalto-cromo [DeguDent (DD) e Vera PDI (VPDI)] foram utilizadas para cada situação experimental. Foram simuladas imersões de 180 dias. As aferições de rugosidade (Ra, μm) tanto em porção metálica quanto em resina acrílica termopolimerizável foram submetidos ao ANOVA e ao teste de Tukey. As alterações superficiais e manchas foram examinadas por meio de microscopia eletrônica de varredura (MEV). Áreas de interesse foram submetidas à espectrometria por energia dispersiva por raios X (EDS). Visualmente, puderam ser verificadas manchas nas superfícies metálicas quando utilizados HS e MI. A rugosidade dos materiais não foi afetada pelas soluções (p>0,05). As fotomicrografias evidenciaram que HS e MI ocasionaram alterações superficiais. As análises de EDS revelaram a presença de oxigênio nos grupos HS e MI, o que pode sugerir que estas duas soluções causaram oxidação das superfícies, provocando pontos de corrosão. Dentre as limitações do presente estudo, pode-se concluir que estas soluções não são apropriadas para a higienização das PPR.

Mass loss of four commercially available heat-polymerized acrylic resins after toothbrushing with three different dentifrices

The association between a toothbrush and a dentifrice is the most used denture cleaning method. The purpose of this study was to evaluate the abrasiveness of specific and non-specific denture cleaning dentifrices on different heat-polymerized acrylic resins. Sixteen specimens (90x30x3mm) of each acrylic resin (QC-20, Lucitone 550, Clássico, Vipi-Cril) were prepared and randomly assigned to 4 groups: 1: control (distilled water), 2: Colgate, 3: Bonyplus and 4: Dentu-Creme. The specimens were subjected to simulated toothbrushing in an automatic brushing machine using 35,600 brush strokes for each specimen. Brushing abrasion run at a 200-g load with the specimens immersed in 2:1 dentifrice/water slurry. Specimens were reconditioned to constant mass and the mass loss (mg) was evaluated. Data were analyzed by 2-way ANOVA and Tukey's test (a=0.05). Analysis of dentifrices' abrasive particles was made by scanning electron microscopy. Colgate produced the greatest mass reduction (42.44 mg, p<0.05), followed by Dentu-Creme (33.60 mg). Bonyplus was the less abrasive (19.91 mg), similar to the control group (19.69 mg) (p>0.05). The mass loss values indicated that QC-20 (33.13 mg) and Lucitone 550 (33.05 mg) resins were less (p<0.05) resistant to abrasion than Clássico (26.04 mg) and Vipi-Cril (23.43 mg). In conclusion, Colgate produced the greatest abrasion. Specific dentifrices for dentures tend to cause less damage to acrylic resins.

Effect of chemical denture cleansers on flexural resistance and color changes of microwave-polymerized acrylic resins

Aim: The aim of this study was to assess the flexural resistance and color alterations of microwave-polymerized acrylic resins immersed in denture cleansers for different periods of time. Methods: Forty-five rectangular specimens (65x10x3mm) of each commercial brand of the microwave-activated acrylic resins (Vipi Wave and Onda Cryl) were divided in three denture cleanser groups (Bony Plus, Corega Tabs and Efferdent Plus) and a control group (immersion in water). Soaking trials of 15 min and 8 h simulated 30 days of use. The flexural strength test was carried out in a universal testing machine. Color alterations were assessed by visual inspection of photographs. The results obtained in the flexural test, in kgf, were converted to MPa and these values were submitted to analysis of variance with a 5% significance level. Results: There were no significant differences (p<0.05) between Onda Cryl (85.61±12.76) and Vipi Wave (89.8±19.95) after the soaking trials regarding the use of different denture cleansers. No differences were found in relation to the solutions [Bony Plus (88.52±9.89), Corega Tabs (88.75±12.71) and Efferdent (85.86±12.11)], soaking periods [control (87.17±12.92), 15 min (88.05±11.74) and 8 h (87.91±10.30)], and interactions during the 30 days of simulated use. Visual inspection did not detect any color alterations. Conclusions: Denture cleansers, when used according to the manufacturers’ instructions, did not cause any mechanical or visual alterations in the microwave-polymerized acrylic resins after a simulated period of 30 days of use.

Assessment of flexural strength and color alteration of heat-polymerized acrylic resins after simulated use of denture cleansers

O objetivo deste estudo foi avaliar a resistência à flexão e alterações de cor de resinas acrílicas termopolimerizáveis imersas em higienizadores de prótese por diferentes períodos de tempo. Corpos-de-prova retangulares (65x10x3mm) de três resinas acrílicas (Lucitone 550, QC-20 e Triplex) foram divididos em três grupos de higienizadores de prótese (Bony Plus, Corega Tabs e Efferdent Plus) e um grupo controle (imersão em água). Foram realizadas imersões por 15 min e 8 horas, simulando 30 dias de uso. O teste de resistência à flexão foi realizado com 105 corpos-de-prova em máquina de ensaios universais. Alterações de cor foram avaliadas por meio de fotografias tiradas de 21 corpos-de-prova. Os resultados de resistência à flexão (em MPa) foram submetidos à análise de variância e teste de Tukey, com nível de significância de 5%. Houve diferenças significantes (p<0.01) entre as resinas Lucitone (89,439 ± 7,962); Triplex (88,024 ± 5,167) and QC-20 (83,379 ± 7,153). Não foram encontradas diferenças significantes (p>0.05) entre os higienizadores de prótese (Bony Plus = 87,693 ± 6,943; Corega Tabs = 86,955 ± 7,114; Efferdent Plus = 86,195 ± 7,865; e controle = 86,536 ± 7.012) nem entre os períodos de imersão (15 min = 86,875 ± 7,625 e 8 h = 87,432 ± 7,355) durante os ciclos de imersão que simularam 30 dias de uso. A inspeção visual não detectou qualquer alteração de cor. Os achados desse estudo revelaram que os higienizadores de prótese, quando usados de acordo com as instruções dos fabricantes, não afetaram a resistência à flexão nem causaram alterações de cor nas resinas acrílicas termopolimerizáveis após um período de uso simulado de 30 dias.